Paint removal example ~ Actual measurement of two PVD vacuum coating stripping methods!! Replace sandblasting!!-Kelly Chemical Electronics Kelly Chemical Electronics
NEWS
2022.06.27

Paint removal example ~ Actual measurement of two PVD vacuum coating stripping methods!! Replace sandblasting!!

PVD Coating Removal Method ~ Compliant with EU REACH Regulations~

 

Replacing Sandblasting! Chemical coating removal is faster and more effective for large quantities of workpieces!

 

PVD refers to the process of depositing the desired coating material onto a workpiece in a vacuum environment, either in gas or plasma form. Due to its versatility and excellent wear and chemical resistance, PVD coatings find applications in various fields including optics, electronics, and semiconductor industries. However, some workpieces may require coating removal for reusability or refurbishment, thus necessitating a coating removal process.

 

Comparison of Three Treatment Methods

 

Treatment Method Replace with New Parts Sandblasting Chemical Coating Removal
Impact on the Part                    Entirely New Parts                            Potential deformation, wear, damage to parts No particular impact
Impact on Production Environment No Impact

Residual powder may contaminate vacuum coating equipment, clean rooms

Process involves water rinsing and drying, no environmental contamination potential
Cost High Low Medium
Labor Low High Medium

 

Optical Molybdenum Electrode Plate Coating Removal

 

Workpiece: Molybdenum electrode plate

Purpose: Accumulated coatings on the surface due to multiple coating procedures, aiming for reusability to reduce costs.

Conditions: Controx E 230 100% original solution, heated to 90°C, reaction time of 15 minutes.

Results: After coating removal, a simple rinse with deionized water reveals the original metallic color of the molybdenum plate.

 

Before Coating Removal:

 

 

After Coating Removal:

 

 

Stainless Steel Component PVD Coating Removal

 

Workpiece: Stainless steel component

Purpose: Processing heavy-duty components, aiming for complete coating removal for re-coating.

Conditions: Controx E 230 100% original solution, heated to 70°C, reaction time of 30 minutes.

Results: After coating removal, a simple rinse with deionized water reveals the original metallic color of the stainless steel, enabling further processing.

 

Before Coating Removal:

 

 

After Coating Removal:

 

諮詢窗口
公隆化學股份有限公司
電子科技事業處
TEL:(02)2762-1985 ext 11200



Kelly's Newsletter~ New Information for you !!

5G low dielectric materials: In the application field of 5G, materials with low dielectric properties have attracted much...(More)

Bio epoxy resins: Under the corporate spirit of all parties seeking ESG, bio-based epoxy resin has low-carbon...(More)

Facebook(另開視窗) 撥打電話+8860227621985 寄信至helpdesk@es-kelly.com